POLYLAN AX4000
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
丙烯腈丁二烯苯乙烯
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
POLYMA Kunststoff GmbH & Co. KG
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Technical Data
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
總體
|
|
|
|
|
|
|
|
|
|
材料狀態(tài)
|
• 已商用：當(dāng)前有效
|
|
|
|
|
|
|
|
|
資料 1
|
• Technical Datasheet (English)
|
|
|
|
|
|
|
|
|
供貨地區(qū)
|
• 歐洲
|
|
|
|
|
|
|
|
|
性能特點(diǎn)
|
• 耐熱性，中等
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
物理性能
|
額定值 單位制
|
測(cè)試方法
|
|
|
|
|
|
|
密度
|
1.05g/cm³
|
ISO 1183
|
|
|
|
|
|
|
熔流率 (200°C/10.0 kg)
|
10g/10 min
|
ASTM D1238
|
|
|
|
|
|
|
ISO 1133
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
機(jī)械性能
|
額定值 單位制
|
測(cè)試方法
|
|
|
|
|
|
|
拉伸模量 (23°C)
|
2550MPa
|
ASTM D638
|
|
|
|
|
|
|
ISO 527-2
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
抗張強(qiáng)度 (屈服, 23°C)
|
39.0MPa
|
ASTM D638
|
|
|
|
|
|
|
ISO 527-2
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
彎曲強(qiáng)度 (23°C)
|
69.0MPa
|
ASTM D790
|
|
|
|
|
|
|
ISO 178
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
沖擊性能
|
額定值 單位制
|
測(cè)試方法
|
|
|
|
|
|
|
懸壁梁缺口沖擊強(qiáng)度 (23°C, 6.35 mm)
|
170J/m
|
ASTM D256
|
|
|
|
|
|
|
硬度
|
額定值 單位制
|
測(cè)試方法
|
|
|
|
|
|
|
洛氏硬度 (R 計(jì)秤, 23°C)
|
106
|
ASTM D785
|
|
|
|
|
|
|
ISO 2039-2
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
熱性能
|
額定值 單位制
|
測(cè)試方法
|
|
|
|
|
|
|
熱變形溫度
|
|
|
|
|
|
|
|
|
|
1.8 MPa, 未退火, 12.7 mm
|
99.0°C
|
ASTM D648
|
|
|
|
|
|
|
1.8 MPa, 未退火
|
99.0°C
|
ISO 75-2/A
|
|
|
|
|
|
|
1.8 MPa, 退火, 12.7 mm
|
110°C
|
ASTM D648
|
|
|
|
|
|
|
1.8 MPa, 退火
|
110°C
|
ISO 75-2/A
|
|
|
|
|
|
|
維卡軟化溫度
|
116°C
|
ISO 306/A
|
3
|
|
|
|
|
|
ASTM D1525
|
|
|
備注