POLYLAN AT5500
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
丙烯腈丁二烯苯乙烯
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
POLYMA Kunststoff GmbH & Co. KG
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Technical Data
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
總體
|
|
|
|
|
|
|
|
|
|
材料狀態
|
• 已商用：當前有效
|
|
|
|
|
|
|
|
|
資料 1
|
• Technical Datasheet (English)
|
|
|
|
|
|
|
|
|
供貨地區
|
• 歐洲
|
|
|
|
|
|
|
|
|
UL 檔案號
|
• E162823
|
|
|
|
|
|
|
|
|
外觀
|
• 清晰/透明
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
物理性能
|
額定值 單位制
|
測試方法
|
|
|
|
|
|
|
密度
|
1.07g/cm³
|
ISO 1183
|
|
|
|
|
|
|
熔流率
|
|
ASTM D1238
|
|
|
|
|
|
|
200°C/10.0 kg
|
26g/10 min
|
ISO 1133
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
200°C/5.0 kg
|
2.1g/10 min
|
|
|
|
|
|
|
|
|
機械性能
|
額定值 單位制
|
測試方法
|
|
|
|
|
|
|
拉伸模量 (23°C)
|
2160MPa
|
ASTM D638
|
|
|
|
|
|
|
ISO 527-2
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
抗張強度 (屈服, 23°C)
|
44.0MPa
|
ASTM D638
|
|
|
|
|
|
|
ISO 527-2
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
彎曲強度 (23°C)
|
72.0MPa
|
ASTM D790
|
|
|
|
|
|
|
ISO 178
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
沖擊性能
|
額定值 單位制
|
測試方法
|
|
|
|
|
|
|
懸壁梁缺口沖擊強度 (23°C, 6.35 mm)
|
150J/m
|
ASTM D256
|
|
|
|
|
|
|
硬度
|
額定值 單位制
|
測試方法
|
|
|
|
|
|
|
洛氏硬度 (R 計秤, 23°C)
|
105
|
ASTM D785
|
|
|
|
|
|
|
ISO 2039-2
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
熱性能
|
額定值 單位制
|
測試方法
|
|
|
|
|
|
|
熱變形溫度
|
|
|
|
|
|
|
|
|
|
1.8 MPa, 未退火, 12.7 mm
|
87.0°C
|
ASTM D648
|
|
|
|
|
|
|
1.8 MPa, 未退火
|
87.0°C
|
ISO 75-2/A
|
|
|
|
|
|
|
1.8 MPa, 退火, 12.7 mm
|
99.0°C
|
ASTM D648
|
|
|
|
|
|
|
1.8 MPa, 退火
|
99.0°C
|
ISO 75-2/A
|
|
|
|
|
|
|
維卡軟化溫度
|
102°C
|
ISO 306/A
|
3
|
|
|
|
|
|
ASTM D1525
|
|
|
|
|
|
可燃性
|
額定值 單位制
|
測試方法
|
|
|
|
|
|
|
UL 阻燃等級 (1.59 mm)
|
HB
|
UL 94
|
|
|
|
備注
1 通過這些鏈接您能夠訪問供應商資料。我們盡量保證及時更新資料；不過您可以從供應商處了解最新資料。
2 一般屬性：這些不能被視為規格。
3 壓 力1 (10N)
|